13-8 Stainless Steel

You can send RFQs by filling out the RFQ form below. Or you can fax RFQs to 800-707-3439. We will get back to you ASAP.

 

* All Trademarks and/or Trade names are the properties of their respective owners.

 

13-8 Stainless Steel Data Sheet
(view complete data sheet for this material - including material property data, metal compositions, etc)

California Metal & Supply is a leading supplier of quality
13-8 Stainless Steel Sheet, 13-8 Stainless Steel Plate, 13-8 Stainless Steel Bar.

Alloy 13-8 PH stainless steel  is a precipitation, age hardenable stainless steel. Stainless Steel 13-8's principal features are toughness, good resistance to general and stress corrosion cracking, and high strength that is developed by a single low temperature heat treatment.

Applications: SS 13-8 has been used in aircraft components such as landing gear and structural sections, valves, shafts, and components in the petrochemical and nuclear industries.

Specifications: Alloy 13-8, UNS S13800

1) 13-8 PH Stainless Steel: AMS 5629, DMS 2100, STM-05-602, STO160LB0013, ASTM-A564 (XM-13), AMS 5864, BMS7-322, RMS 150, PWA/LCS, GE S400, AMS-H-6875, AMS 2759, AISI 632, ASTM-A693 (XM-13), ASTM-A705 (XM-13), DIN 1.4534, UNS S13800, Werkstoff 1.4548

13-8 Solution Annealed Round Bar Per AMS 5629 Type 1 (Heat treated to H1025)

13-8 Stainless Steel Plate Per AMS 5629, ASTM A-564/693, AMS 5864

13-8 Stainless Steel Flat Bar Per AMS 5629, Can be heat treated to H1000 Per AMS 2759/3 DMS 2100

13-8 Stainless Steel Round Bar Per AMS 5629, Can be heat treated to H1000 Per AMS 2759/3

UNS S13800, Capable of ASTM-A564, Centerless Ground Bar

13-8 Stainless Steel Square Bar Per AMS 5268

13-8 Stainless Steel Hex Bar Per AMS 5268


All of our Alloy 13-8 PH stainless steel is ordered to specific thickness. We supply 13-8 PH stainless steel and are capable of fulfilling your required lengths and widths. California Metal & Supply Inc. also has a stocking program to support long term contract for your 13-8 PH stainless steel needs.
 

      

Specifications for Alloy 13-8 PH Stainless Steel
 

Bar AMS 5629 Type 1, ASTM A 564 Grade XM13, ASME SA564 Grade XM13, DMS 2100,    HMS 6 1105,  HMS 6 1105 Exc Sonic, Sonic Per MIL STD 2154 Class A, STM-05-602, STO 160 LBO 013
Plate AMS 5864, ASTM A 564, ASME SA693
Wire ASTM A 564, ASME SA564
Sheet ASTM A693, ASME SA693
Strip ASTM A693, ASME SA693
Forgings ASTM A 705, ASME SA705
Rings AMS 5629
Extrusions AMS 5629

   

Typical Mechanical Properties for Alloy 13-8 PH Stainless Steel (Room Temperature)
 

13-8 Sol Tr

Condition  Yield Strength (0.2%) ksi Ultimate Tensile strength ksi Elongation % in 2" % Reduction of Area

 Rockwell C

 Hardness

H 950 210 225 12 40 47
H 1000 205 215 13 50 45
H 1050 180 190 15 55 43
H 1100 150 160 18 60 35
H 1150 105 145 20 63 33
H 1150 M 85 130 22 70 32

Alloy 13-8 Supplied in Solution Treated Condition.

Machinability for Alloy 13-8 PH Stainless Steel

This is a tough machining stainless steel. Although it can be machined in all conditions, best results can be obtained in condition H1150M. Compared to type 304 stainless, speeds should be roughly 25 % lower for optimum tool life and finish.

Forming for 13-8 PH Stainless Steel

This alloy can be formed using conventional techniques with the degree of formability being limited only by its high initial yield strength.

Welding for 13-8 PH Stainless Steel

Best welded in the solution annealed condition, using 13-8 MO filler material. Both resistance and inert gas shielded methods are acceptable.


      

Heat Treatment for Alloy 13-8 PH Stainless Steel

CONDITION A--Soak at 1700 F (927 C) and cool below 60 F (16 C) for 1 hour. CONDITION RH 950- Treat Condition A material at -100 F(-73C) for 2 hours, air warm to room temperature (within 24 hours of solution treatment). Then heat cold treated material to 950 F(510 C) for 4 hours and air cool. CONDITION H950, H1000, H1050, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.

Forging for Alloy 13-8 PH Stainless Steel

Soak at 2150 F(1177 C) for 1 hour prior to forging. Do not work below 1750 F(954 C). All forgings should be solution treated prior to final hardening. Air cool to room temperature after forging.

Hot Working for Alloy 13-8 PH Stainless Steel

13-8 can be satisfactorily hot worked. Hot worked material must be solution annealed prior to hardening for reliable results.

Cold Working for Alloy 13-8 PH Stainless Steel

Despite its high initial yield strength, this alloy can be satisfactorily cold worked.
 

Stainless Steel Sheet, Plate, Bar & Tubing

1) 13-8 PH Stainless Steel: AMS 5629, DMS 2100, STM-05-602, STO160LB0013, ASTM-A564 (XM-13), AMS 5864, BMS7-322, RMS 150
2) 15-5 PH Stainless Steel: AMS 5659, BMS 7-240, AMS 5862, ASTM-A564 (XM-12)
3) 17-4 PH Stainless Steel: AMS 5643, AMS 5604, AMS 5622, ASTM-A564 (TYPE 630), UNS S17400
4) 17-7 PH Stainless Steel: AMS 5644, AMS 5528, AMS 5529, MIL-S- 25043, UNS S17700
5) A286 Stainless Steel: AMS 5525, AMS 5726, AMS 5731, AMS 5732, AMS 5734, AMS 5737, AMS 5804, AMS 5805, AMS 5853, AMS 5858, AMS 5895, ASTM-A-453, Gr 660 CL. B, PWA/LCS
6) 301 Stainless Steel: AMS 5517, AMS5518, AMS 5519, AMS 5901, 301 1/2 Hard Stainless Steel Per AMS 5518, 301 ANN: AMS 5515
7) 302 Stainless Steel: AMS 5516, AMS 5636, UNS S30302
8) 303 SU Stainless Steel: AMS 5640 TYPE 1, MIL-S-7720, ASTM-A582, AMS-S-7720, 303 Stainless Steel Round Bar x 12 FT
9) 303 SE Stainless Steel: AMS 5640 TYPE 2, AMS 5641, MIL-S-7720, ASTM-A582
10) 304 / 304L Stainless Steel: QQ-S-763, AMS 5639, AMS 5513, ASTM-A240, 304 / 304L Stainless Steel Plate Per AMS 5511, 304 / 304L Corrosion & Heat Resistant Alloy, Cold Finished & Annealed Per ASTM-A580
11) 321 Stainless Steel: QQ-S-763, AMS 5645, AMS 5510, ASTM-A240, 321 2D Finish Stainless Steel Sheet Per AMS 5510
12) 330 Stainless Steel: RA330, RA 330 UNS08330, EN 1.4886, ASME-B536, ASME-B511, ASTM SB-563, ASTM SB-511, ASTM SB-535, ASTM-B535, AMS 5592, AMS 5716, N08334, W88334, Seamless Pipe Sch 40
13) 347 Stainless Steel: 347 Stainless Steel Sheet, AMS 5512, UNS S34700, UNS S34709, ASTM A 240, ASME SA 240, ASTM A262 Practice E, AMS 5646, AMS 5680, ASTM A182, ASTM A276, ASTM A314, ASTM A473, ASTM A 269, ASTM A 479, QQS 763, ASME SA182, EN10204 DIN3.1B, MSRR 5632, PWA 300, PWA F17 LCS, W. Nr./EN 1.4550
14) 403/410 Stainless Steel: AMS 5612, AMS 5613, GE B50A459B-S6, 410 Stainless Steel Welded Pipe
15) 440C Stainless Steel: QQ-S-763, AMS 5630, ASTM-A276
16) 450 Stainless Steel: GE B50A789A-S13
17) 904L Stainless Steel: UNS N08904, 904L Tubing, 904L Stainless Steel Tube Per ASTM-A213, NACE MR0175
Alloy 904L tubing is a low carbon high alloy austenitic stainless steel, for use in applications that require moderate to high corrosion resistance.  904L tubing is non-magnetic in all conditions, possesses amazing toughness, and has good formability and weldability.

* Nitronic 60, also considered a Super Alloy, is designed to be the best non-galling stainless steel.

 

Please fill out the RFQ form below. We will get back to you ASAP. Thanks.

 

Please enter Material information such as spec., size, q'ty below.

Information (Size, Spec., Q'ty)

Name:

Company:

Email Address:  (Don’t forget to enter. Please use company email address)

Phone Number:

Fax Number:

<= Choose the type of quote

Comments:

 

 

 

 

* Visa, MasterCard, American Express & Discover
For your convenience, we accept Visa, Master, Amex & Discover. We also accept PayPal.

Please contact sales department if you have any questions regarding payment methods.

 

Demandbase Connect